V.C.T.I. Heat Resistant and Thermal Insulation Paint

Product Description

UGAM VCTI COATING

DESCRIPTION:

1) The Product is mainly used for reducing the surface temperatures of hot surfaces like Exterior of boilers.

2) When there is heavy heat losses through boiler surfaces, UGAM V C T I coating is the best solution to arrest the same. 

3) Approximately 30 to 50 mm thick coating is to be applied depending upon the surface temperature. Our technical team will provide you the guidance on the same.

4) This is also used for reducing the surface temperatures of steam lines, hot water lines, hot gasses lines, hot oil lines etc. 

5) The pipelines are coated over with UGAM V C T I coating to bring the temperatures to ambient. 

6) This also provides energy saving and increased efficiency due to blocking of heat losses. 

7) This is ideally suitable for reducing surface temperatures of furnaces and tobring it to near to ambient.

8) The Product is mainly used for reducing the surface temperatures of hot surfaces like Exterior of boilers. When there is heavy heat losses through boiler surfaces, UGAM V C T I coating is the best solution to arrest the same. Approximately 30 to 50 mm thick coating is to be applied depending upon the surface temperature. Our technical team will provide you the guidance on the same.

9) This is also used for reducing the surface temperatures of steam lines, hot water lines, Hot gasses lines, hot oil lines etc. The pipelines are coated over with UGAM V C T I Coating to bring the temperatures to ambient. This also provides energy saving and Increased efficiency due to blocking of heat losses.

10) This is ideally suitable for reducing surface temperatures of furnaces and to bring it to near to ambient.

Surface Preparation:

1) UGAM V.C.T.I. can be applied to bare steel, provided that the surface is clean, free from oil, dust, loose mill scale, loose rust, or any other contamination. The contractor is responsible for ensuring that the steel surfaces are in a suitable state to receive UGAM V.C.T.I.

2) Cleaning can be effected by using brushes, industrial brushes, industrial vacuum cleaners etc. Oils and greases can be removed by steam cleaning or water jetting using suitable detergent solutions.

3) The pH value of UGAM V.C.T.I. is 12 at the time of application.  This has  the advantage  of imparting  a degree of corrosion protection  to bare steel members,  provided that the  sprayed coating  remains dry  in use,  as will  usually apply for internal applications.   In the case of UGAM V.C.T.I. External Grade,  which  is  going  to  be  permanently exposed to the elements,  in addition to any protective treatment to the steel on erection, a final protective paint coating will be required over the completed UGAM V.C.T.I. Layer. In any case, we suggest application of UGAM V C PRIMER to bare steel before application of UGAM V.C.T.I.

4) A "prick-up" coat  is recommended  to all  painted surfaces,  however, certain paints, e.g. alkyd based primers, can be degraded by the alkalinity of cement, and where surfaces have been so painted it is recommended  that the advice  of the paint manufacturer  should be  obtained.   If this advice cannot be obtained, or if there is any doubt as to the suitability of the given paint, the painted surface should ALWAYS be treated with a coating of UGAM V C PRIMER.

5) On galvanized steel an etch primer should be used, followed by a coat of UGAM V C PRIMER.

6) Aluminium surfaces are alkali sensitive and require treatment with an etch primer,   again followed by a coat of UGAM V C Primer.

7) Concrete surfaces should be cleaned by the removal of dust,  and all traces  of oil and grease, including any mould release agents.  If painted, follow the specification in 3.4 above.

8) Before the commencement of spraying,  complete  any necessary  masking  to protect  specific areas from overspray.